Ukucaciswa Okwenziwe Ngokwezifiso 1-0mm 3-1mm 5-3mm 8-5mm Blasting Media Fused Mullite Grains 79% Molten Mullite Grits
Funda kabanzi- Isimo Somkhiqizo:Amabhulokhi Amhlophe/Ampunga/Ama-Grits/Isihlabathi/Ufulawa
- Imininingwane:1-0mm; 3-1mm; 5-3mm; 8-5mm
- Izicelo:Okungaguquki, okungaphonswa, ukuqhumisa, ukugaya, ukugoqa, ukwelashwa kwendawo, ukupholisha
- Ukupakisha:25 kg/isikhwama sepulasitiki 1000 kg/isikhwama sepulasitiki ngokuzikhethela komthengi
- I-Al2O3% ≥:74-79%
- I-SiO2:20-25%
- I-Fe2O3:≤0.1%
- Ubuningi Bangempela:3.10 g/cm3min
- Indawo Yokuncibilika:1830°C
-
Izinhlayiya ze-Carbide ze-Silicon Green ezisebenza kahle kakhulu kanye nama-Grits
Funda kabanzi- (AlO2):≈ 95.5%
- Indawo yokuncibilika:2,000° C
- (SiO2) Akukho Mahhala:0.67%
- (Fe2):0.25%
- Ifomu lekristalu:I-Alpha Alumina
- Amandla adonsela phansi aqondile:3.95 grm/cc
- Ubuningi:132 lbs/ft3 (kuya ngosayizi)
- Ubulukhuni::I-KNOPPS = 2000, i-MOHS = 9
- Indawo Yokuncibilika:2,000° C
-
I-Silicon Carbide Eluhlaza Echotshoziwe Esezingeni Eliphezulu Yokupholisha Nokugaya
Funda kabanzi- (AlO2):≈ 95.5%
- Indawo yokuncibilika:2,000° C
- (SiO2) Akukho Mahhala:0.67%
- (Fe2):0.25%
- Ifomu lekristalu:I-Alpha Alumina
- Amandla adonsela phansi aqondile:3.95 grm/cc
- Ubuningi:132 lbs/ft3 (kuya ngosayizi)
- Ubulukhuni::I-KNOPPS = 2000, i-MOHS = 9
- Indawo Yokuncibilika:2,000° C
-
I-Green Silicon Carbide Powder ye-Bonded Silicon Carbide Grinding Wheel
Funda kabanzi- (AlO2):≈ 95.5%
- Indawo yokuncibilika:2,000° C
- (SiO2) Akukho Mahhala:0.67%
- (Fe2):0.25%
- Ifomu lekristalu:I-Alpha Alumina
- Amandla adonsela phansi aqondile:3.95 grm/cc
- Ubuningi:132 lbs/ft3 (kuya ngosayizi)
- Ubulukhuni::I-KNOPPS = 2000, i-MOHS = 9
- Indawo Yokuncibilika:2,000° C
-
I-White Corundum JIS/White Fused Alumina/Wa Abrasive
Funda kabanzi- I-AlO3:99.5%
- I-TiO2:0.0995%
- I-SiO2 (ayikhululekile):0.05%
- I-Fe2:0.08%
- I-MgO:0.02%
- I-Alkali (i-Soda ne-Potash):0.30%
- Ifomu lekristalu:Iklasi le-Rhombohedral
- Uhlobo Lwekhemikhali:I-Amphoteric
- Amandla adonsela phansi aqondile:3.95 grm/cc
- Ubuningi:116 lbs/ ft3
- Ubulukhuni:I-KNOPPS = 2000, i-MOHS = 9
- Indawo Yokuncibilika:2,000°C
-
I-Aluminium Oxide Ehlanganisiwe Ensundu I-Alumina Ensundu I-Aluminium Oxide Ehlanganisiwe Ensundu I-Aluminium Oxide Ehlanganisiwe Ensundu
Funda kabanzi- (AlO2):≈ 95.5%
- Indawo yokuncibilika:2,000° C
- (SiO2) Akukho Mahhala:0.67%
- (Fe2):0.25%
- Ifomu lekristalu:I-Alpha Alumina
- Amandla adonsela phansi aqondile:3.95 grm/cc
- Ubuningi:132 lbs/ft3 (kuya ngosayizi)
- Ubulukhuni::I-KNOPPS = 2000, i-MOHS = 9
- Indawo Yokuncibilika:2,000° C